You may want to read up on metal embrittlement by hydrogen before thinking it's a simple solution.
When in the steel industry we used ultrasonic NDT equipment that would detect internal hydrogen cracking that some grades of low alloy steel were susceptible to. Steel for safety critical use was scrapped. We could also detect internal defects in free machining steels due to poor distribution of sulphur or lead.